Riblene® FL 23
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Riblene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gChPZ4_Riblene-FL-23.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Riblene FL 23 is a low density polyethylene (LDPE) additivated with slip agent, ideal for blown film extrusion. Riblene FL 23 is characterised by a good balance between proc-essability and mechanical properties. Films manufactured with Riblene FL 23 are easily heat shrinkable and characterised by good optical and mechanical properties. Main Application Riblene FL 23 is recommended for general blown film applications, for the production of low gauge film and shrink film, for lamination and for blending. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.13 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Film Thickness - Recommended / Available | 25 to 80 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 40 µm, Blown Film | 180 | MPa | |
| 1% Secant, TD : 40 µm, Blown Film | 190 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, Blown Film | 11.0 | MPa | |
| TD : Yield, 40 µm, Blown Film | 11.0 | MPa | |
| MD : Break, 40 µm, Blown Film | 25.0 | MPa | |
| TD : Break, 40 µm, Blown Film | 22.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm, Blown Film | 300 | % | |
| TD : Break, 40 µm, Blown Film | 650 | % | |
| Dart Drop Impact 1(40 µm, Blown Film) | 130 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 40.0 µm | 80.0 | kN/m | |
| TD : 40.0 µm | 55.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.0 | °C | ISO 306/A |
| Melting Temperature | 113 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 72 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 5.5 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 190 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 2580 FR | RTP Company | PC+ABS | RTP |
| TAROPRENE® 1 A85 E1N | Taro Plast S.p.A. | TPV | TAROPRENE® |
| UBE Polyethylene F522N | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| Crastin® LW9320 NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Jiangsu Sinarise EX8534X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |