MAJORIS PBT 9237 3030 FB BLACK 8229
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gCWqNP_MAJORIS-PBT-9237-3030-FB-BLACK-8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PBT 9237 3030 FB BLACK 8229 is a 30 % glass fibre/bead reinforced polybutylene terephthalate , intended for injection moulding. The product is available in black and natural (PBT 9237 3030 FB) but other colours can be provided on request. They combine high mechanical, thermal and electrical properties with excellent chemical resistance and dimensional stability. APPLICATIONS PBT 9237 3030 FB BLACK 8229 is intended for the injection moulding of electrical components and automotive applications including interior, exterior and electrical and mechanical systems, such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.1 - 1.5 | % | ISO 294-4 |
| Flow direction | 0.70 - 1.1 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.040 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.13 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 122 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 6600 | MPa | ISO 178 |
| Flexural Stress | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 218 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 209 | °C | ISO 75-2/A |
| Ball Indentation Temperature | 215 | °C | NF C 62-411 |
| Melting Temperature (DSC) | 225 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 37 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.30 | ASTM D150 | |
| 1 kHz | 3.30 | ASTM D150 | |
| 1 MHz | 3.20 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 2.0E-3 | ASTM D150 | |
| 1 kHz | 2.0E-3 | ASTM D150 | |
| 1 MHz | 0.013 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm, 30 sec) | 650 | °C | IEC 60695-2-13 |
| Oxygen Index | 19 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 255 - 270 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Back Pressure: Moderate |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ LB50 | Mando Advanced Materials Co., Ltd. | Nylon 6 | SEPAZ™ |
| TECHNYL® C 246M NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| VESTAMID® NRG 4901 black | Evonik Industries AG | Nylon 12 | VESTAMID® NRG |
| Cheng Yu NG1100S | Cheng Yu Plastic Company Limited | Nylon 66 | Cheng Yu |
| Generic Polyolefin, Unspecified - Calcium Carbonate | Generic | Polyolefin, Unspecified | Generic |