Order Products : sales@su-jiao.com
HiFill® PA6 IM 811 HS L
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gBxa5r_HiFill-PA6-IM-811-HS-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill® PA6 IM 811 HS L is a Polyamide 6 (Nylon 6) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.07 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.80 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | 1.5 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (Yield) | 48.3 | 41.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 230 | 300 | % | ASTM D638 |
| Flexural Modulus | 1210 | 862 | MPa | ASTM D790 |
| Flexural Strength | 58.6 | 51.7 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | No Break | No Break | ASTM D256 | |
| Unnotched Izod Impact (3.18 mm) | No Break | No Break | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 166 | -- | °C | |
| 1.8 MPa, Unannealed | 51.7 | -- | °C | |
| CLTE - Flow | 2.3E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 2.0E+13 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 17 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Additional Information | Dry | Conditioned | ||
|---|---|---|---|---|
| TPCI # | 6109102 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 254 to 291 | °C | |
| Middle Temperature | 254 to 291 | °C | |
| Front Temperature | 254 to 291 | °C | |
| Processing (Melt) Temp | 238 to 277 | °C | |
| Mold Temperature | 65.6 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 5310 | SABIC Innovative Plastics | PP, Unspecified | SABIC® PPcompound |
| SLOVALEN® PC 82 T 30 | Plastcom | PP, Unspecified | SLOVALEN® |
| Nipol® DN631 | Zeon Chemicals L.P. | NBR | Nipol® |
| TECACOMP® PA66 TC black 4028 | Ensinger GmbH | Nylon 66 | TECACOMP® |
| 3M™ Dyneon™ PTFE Compound 1191 N | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |