Nypol® PA B3 HF NTLA010 NT324
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gBdAAf_Nypol-PA-B3-HF-NTLA010-NT324.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 natural, fast flow, good set of thermal properties, electrical and mechanical. Ideal for injection molding. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.13 to 1.15 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0 to 1.5 | -- | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.7 | -- | % | ASTM D570 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3500 | -- | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | |||
| Yield | 85.0 | -- | MPa | |
| -- | 70.0 | 60.0 | MPa | |
| Tensile Elongation | ASTM D638 | |||
| Yield | 4.0 | -- | % | |
| Break | 40 | 110 | % | |
| Flexural Modulus | 3000 | 1500 | MPa | ASTM D790 |
| Flexural Strength | 100 | 50.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 60 | 90 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 70.0 | -- | °C | ASTM D648 |
| Vicat Softening Temperature | 205 | -- | °C | ASTM D1525 1 |
| Melting Temperature | 210 to 225 | -- | °C | ASTM D2117 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 220 to 240 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO K3004 | Formosa Plastics Corporation | PP Impact Copolymer | TAIRIPRO |
| Trexlink™ 6770 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | Trexlink™ |
| Unilex™ UP 1112C | United Polychem | PP Random Copolymer | Unilex™ |
| Novamid® 2030A-8 | DSM Engineering Plastics | Nylon 66/6 | Novamid® |
| Dryflex® PCW 80A651B | ELASTO | TPE | Dryflex® |