| Texin RxT85A resin is an aromatic polyether-based thermoplastic polyurethane. It can be processed by injection molding, extrusion or blow molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/8.7 kg) | 4.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 2.54mm | 0.80 | % | ASTM D955 |
| Transverse flow : 2.54mm | 0.80 | % | ASTM D955 |
| Vertical flow direction : 2.54mm | 0.80 | % | ISO 2577 |
| Flow direction : 2.54mm | 0.80 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | |||
| 23°C | 29.9 | MPa | ASTM D790 |
| 23°C | 26.9 | MPa | ISO 178 |
| Taber Abrasion Resistance | |||
| 1000 Cycles, 1000g, H-18 wheel | 30.0 | mg | ISO 4649 |
| 1000 Cycles, 1000g, H-18 wheel | 30.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| 100% strain | 5.50 | MPa | ASTM D412, ISO 37 |
| 300% strain | 9.70 | MPa | ASTM D412, ISO 37 |
| Tensile Strength (Yield) | 36.6 | MPa | ASTM D412, ISO 37 |
| Tensile Elongation (Break) | 610 | % | ASTM D412, ISO 37 |
| Tear Strength | |||
| -- 1 | 87.6 | kN/m | ASTM D624 |
| -- | 88 | kN/m | ISO 34-1 |
| Compression Set 2 | ASTM D395B, ISO 815 | ||
| 23°C, 22 hr | 16 | % | ASTM D395B, ISO 815 |
| 70°C, 22 hr | 40 | % | ASTM D395B, ISO 815 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 80.0 | °C | ISO 306/50, ASTM D1525 3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index | |||
| -- | < 10 | YI | DIN 6167 |
| -- | < 10 | YI | ASTM E313 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 93.0 - 104 | °C | |
| Drying Time - Desiccant Dryer | 2.0 | hr | |
| Suggested Max Moisture | < 0.030 | % | |
| Rear Temperature | 193 - 204 | °C | |
| Middle Temperature | 196 - 207 | °C | |
| Front Temperature | 196 - 207 | °C | |
| Nozzle Temperature | 199 - 210 | °C | |
| Processing (Melt) Temp | 199 - 210 | °C | |
| Mold Temperature | 16.0 - 38.0 | °C | |
| Injection Pressure | 41.4 - 103 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | < 5.52 | MPa | |
| Screw Speed | 40 - 80 | rpm | |
| Cushion | < 3.18 | mm |
| Injection instructions |
|---|
| Hold Pressure: 60 to 80% of Injection Pressure |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.0 - 104 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 182 - 193 | °C | |
| Cylinder Zone 2 Temp. | 193 - 204 | °C | |
| Cylinder Zone 3 Temp. | 193 - 204 | °C | |
| Melt Temperature | 199 - 210 | °C | |
| Die Temperature | 193 - 210 | °C |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | Post-cured 16 hr at 230°F |
| 3 . | 速率 A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3590 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| TAIRILAC ANC100 | Formosa Plastics Corporation | ABS | TAIRILAC |
| Ferro PP NPP00GC25WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| DuraForm® GF | 3D Systems | Nylon, Unspecified | DuraForm® |
| Polifil® Nylon 89MRGFHS | The Plastics Group | Nylon 6 | Polifil® Nylon |