LNP™ LUBRICOMP™ GFL36 compound
| Category: | PSU , Polysulfone |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gAtIhN_LNP-LUBRICOMP-GFL36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP GFL36 is a compound based on Polysulfone resin containing Glass Fiber, PTFE. Added features include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound GFL-4036 Product reorder name: GFL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.58 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 92.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.6 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 7400 | MPa | ISO 178 |
| Flexural Stress | 132 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 185 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.7E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 4.4E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 327 to 338 | °C | |
| Middle Temperature | 338 to 349 | °C | |
| Front Temperature | 349 to 360 | °C | |
| Processing (Melt) Temp | 360 to 371 | °C | |
| Mold Temperature | 149 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Microthene® G MN72700 | LyondellBasell Industries | LDPE | Microthene® G |
| Zytel® RS 30G30L NC010 | DuPont Performance Polymers | Nylon 610 | Zytel® RS |
| ALTECH® PA6 A 1000/109 BK1011-13LSC | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Andur 8003 AS/Ethacure® 100LC | Anderson Development Company | PUR-TDI | Andur |
| Generic Nylon 66 - Proprietary | Generic | Nylon 66 | Generic |