TRANSMARE® 35HNF50-0.001
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gA3Q9v_TRANSMARE-35HNF50-0-001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 35HNF50-0.001 is a 50% bamboo fiber reinforced polypropylene homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.2 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 78 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (4.00 mm) | 5050 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 4.00 mm, Injection Molded) | 43.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 4.00 mm, Injection Molded) | 1.6 | % | ISO 527-2/50 |
| Flexural Modulus | 4960 | MPa | ISO 178 |
| Flexural Stress | 68.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40°C | 2.5 | kJ/m² | ISO 179/1A |
| 0°C | 3.0 | kJ/m² | ISO 179/1A |
| 23°C | 3.4 | kJ/m² | ISO 179/1A |
| Charpy Unnotched Impact Strength | ISO 179/1U | ||
| -40°C | 7.3 | kJ/m² | ISO 179/1U |
| 23°C | 9.2 | kJ/m² | ISO 179/1U |
| Notched Izod Impact (23°C) | 3.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 9.3 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 148 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 103 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 163 | °C | ISO 306/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 150 | °C | |
| Middle Temperature | 160 | °C | |
| Front Temperature | 175 | °C | |
| Nozzle Temperature | 180 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| In specific cases pre-drying of this material might be required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AESNO 14 TL | Arkema | Nylon 12 | Rilsamid® |
| RTP 201.3 UV | RTP Company | Nylon 66 | RTP |
| Silopren® Gel TP3636 | Momentive Performance Materials Inc. | Silicone Rubber, RTV-2 | Silopren® |
| Bio-Flex® F 2201 CL | FKuR Kunststoff GmbH | PLA | Bio-Flex® |
| FORMEX® GK-62 | ITW FORMEX | PP, Unspecified | FORMEX® |