Sarlink® TPE RV-2235B
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g9CAv0_Sarlink-TPE-RV-2235B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sarlink RV-2235B is a high performance Thermoplastic Elastomer used in transportation applications. Sarlink RV-2235B is a low hardness grade and UV resistant. This grade can be processed by extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shore A, 1 second, injection molding | 44 | ISO 868 | |
| Shore A, 5 seconds, injection molding | 42 | ISO 868 | |
| Shore A, 15 seconds, injection molding | 41 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Transverse flow : 100% strain | 0.730 | MPa | ISO 37 |
| Flow : 100% strain | 1.90 | MPa | ISO 37 |
| Tensile Stress 2 | ISO 37 | ||
| Transverse flow : Fracture | 6.20 | MPa | ISO 37 |
| Flow : Fracture | 2.40 | MPa | ISO 37 |
| Tensile Elongation 3 | ISO 37 | ||
| Transverse flow : Fracture | 870 | % | ISO 37 |
| Flow : Fracture | 240 | % | ISO 37 |
| Tear Strength 4 | ISO 34-1 | ||
| Transverse flow | 12 | kN/m | ISO 34-1 |
| Flow | 23 | kN/m | ISO 34-1 |
| Compression Set 5 | ISO 815 | ||
| 23°C, 22 hr | 11 | % | ISO 815 |
| 70°C, 22 hr | 60 | % | ISO 815 |
| 90°C, 70 hr | 71 | % | ISO 815 |
| 125°C, 70 hr | 84 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 6 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | 40 | % | ISO 188 |
| Flow : 110°C, 1008 hr | 0.0 | % | ISO 188 |
| Transverse flow : 100% strain 110°C, 1008 hr | 11 | % | ISO 188 |
| Flow : 100% strain 110°C, 1008 hr | 9.5 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | -42 | % | ISO 188 |
| Flow : 125°C, 168 hr | -4.2 | % | ISO 188 |
| Transverse flow : 100% strain 125°C, 168 hr | -2.7 | % | ISO 188 |
| Flow : 100% strain 125°C, 168 hr | 5.3 | % | ISO 188 |
| Change in Tensile Strain at Break in Air 7 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | 9.4 | % | ISO 188 |
| Flow : 110°C, 1008 hr | 42 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | 95 | % | ISO 188 |
| Flow : 125°C, 168 hr | 41 | % | ISO 188 |
| Change in Shore Hardness in Air | |||
| Support a, 110°C, 1008 hr 8 | 3.5 | ISO 188 | |
| Support a, 110°C, 1008 hr 9 | 3.1 | ISO 188 | |
| Support a, 125°C, 168 hr 10 | 2.1 | ISO 188 | |
| Support a, 125°C, 168 hr 11 | 2.3 | ISO 188 | |
| Support a, 125°C, 168 hr 12 | 2.2 | ISO 188 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 209 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 182 - 232 | °C | |
| Middle Temperature | 188 - 238 | °C | |
| Front Temperature | 193 - 243 | °C | |
| Nozzle Temperature | 199 - 249 | °C | |
| Processing (Melt) Temp | 199 - 249 | °C | |
| Mold Temperature | 35.0 - 48.9 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 182 - 232 | °C | |
| Cylinder Zone 2 Temp. | 188 - 238 | °C | |
| Cylinder Zone 3 Temp. | 193 - 243 | °C | |
| Cylinder Zone 5 Temp. | 199 - 249 | °C | |
| Die Temperature | 199 - 249 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 30 to 100 rpm |
| Note Message | |
|---|---|
| 1 . | Type 1, 510mm/min |
| 2 . | Type 1, 510mm/min |
| 3 . | Type 1, 510mm/min |
| 4 . | B method, right angle specimen (without cut), 510mm/min |
| 5 . | Type a |
| 6 . | Type 1 |
| 7 . | Type 1 |
| 8 . | 5 sec delay |
| 9 . | 1 sec |
| 10 . | 1 sec |
| 11 . | 15 sec delay |
| 12 . | 5 sec delay |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen P 9422-67728 | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® Vestolen P |
| ADDILENE H 590 RM20 F | ADDIPLAST | PP, Unspecified | ADDILENE |
| DuraGrip® DGR 6830NC | Advanced Polymer Alloys | TPE | DuraGrip® |
| HiFill® PA6/6 CM16 HS BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| INVISION™ TX 5173U | A. Schulman Inc. | TPV | INVISION™ |