Toyolac® 920-555
| Category: | MABS , Methyl Methacrylate / ABS |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g8hiRA_Toyolac-920-555-79421.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac® 920-555 is a Methyl Methacrylate / ABS (MABS) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.09 | g/cm³ | ASTM D792 |
| 23°C | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 115 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 48.0 | MPa | ASTM D638 |
| 23°C | 54.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 20 | % | ASTM D638 |
| Break, 23°C | 17 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2160 | MPa | ASTM D790 |
| 23°C | 2260 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 74.0 | MPa | ASTM D790 |
| 23°C | 77.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 110 | J/m | |
| 23°C, 12.7 mm | 110 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 83.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 77.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 90.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Total, 3000 µm) | 88.0 | % | ISO 13468 |
| Haze (3000 µm) | 2.0 | % | ISO 14782 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUNGSOX® PP 1040U | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| Nypol® PA B3 G30 HL UV PRTA011 NT341 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Glastherm® CH | Glastic Corporation | Polyester, TS | Glastherm® |
| Sylvin 8685-60 Orange 583 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| POCAN® BF 4215 000000 | LANXESS Corporation | PBT | POCAN® |