| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | BCC Products Inc. |
| Trademark: | BCC Resins |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g8aVLw_BCC-Resins-BC-6126.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BC 6126 is a gray, low toxicity, aluminum filled, epoxy surface coat. This thixotropic resin system provides excellent surface duplication along with vertical coverage to 1/16" thickness. This heat resistant system may be used at room temperature without post-curing. For use above 150°F a post-cure is required. Post cure for applications requiring temperatures above 150°F can be accomplished in an oven or in use by a gradual heat rise; 2 hours @ 150°F, plus 2 hours @ 250°F, plus 2 hours at 300°F. BC 6126 can afford consistent use to 300°F if required. BC 6126 was engineered to replace VCHD and MDA systems while retaining excellent heat resistance. Typical uses include constructing vacuum form tools, Injection and compression molds, RTM and RIM molds, and matched dies. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792, ASTM D1505 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Ultimate) | 40.0 | MPa | ASTM D638 |
| Flexural Strength (Break) | 44.8 | MPa | ASTM D790 |
| Compressive Strength | 193 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 144 | °C | ASTM D648 |
| CLTE - Flow | 4.2E-5 | cm/cm/°C | ASTM D696 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 10, Mix Ratio by Volume: 15 | ||
| Resin | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Pot Life (24°C) | 45 | min | |
| Demold Time (24°C) | 720 to 960 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® FM-LK256 | Sumitomo Bakelite Co., Ltd. | PPS | Sumikon® |
| K-Prene 7000 XL 50 | Technovinyl Polymers India Ltd. | TPV | K-Prene |
| Jamplast Ex-02 ABS | Jamplast, Inc. | ABS | Jamplast |
| MACOMASS PP MM-PP GF 30 | MACOMASS Verkaufs AG | PP, Unspecified | MACOMASS PP |
| Sylvin 2900-80 Clear 8391 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |