Staramide ACF4
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g8RpDf_Staramide-ACF4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide ACF4 is a 20 % Carbon Fiber Reinforced Polyamide 66 injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.10 to 0.15 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 5.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 190 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 12500 | MPa | ISO 178 |
| Flexural Stress | 280 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3 | ISO 180/1A | ||
| -40°C | 5.0 | kJ/m² | |
| -20°C | 6.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 255 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 250 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 255 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.7E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 5 | > 1.8E+5 | ohms | IEC 60093 |
| Volume Resistivity | > 1.8E+5 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by E2P) | HB | UL 94 | |
| Oxygen Index | 27 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 120*10*4 |
| 5 . | ROA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GS1861-N1(PTFE) | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Nipol® LX851F2 | Zeon Corporation | Latex | Nipol® |
| Advanced Composites ADX-2001 | Advanced Composites, Inc. | PP, Unspecified | Advanced Composites |
| Hanwha Total PP HS120 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Sylvin 7844-70C Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |