PPR PPCO08
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Premier Plastic Resins, Inc. |
| Trademark: | PPR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g8EDdA_PPR-PPCO08.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene Copolymer 30 Melt 2 Izod Black |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.908 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.4 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 24.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 12 | % | ASTM D638 |
| Flexural Modulus - Tangent | 1100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 88.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 54.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 38.0 - 71.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 193 - 232 | °C | |
| Middle Temperature | 188 - 227 | °C | |
| Front Temperature | 188 - 227 | °C | |
| Nozzle Temperature | 199 - 221 | °C | |
| Processing (Melt) Temp | 193 - 232 | °C | |
| Mold Temperature | 16.0 - 54.0 | °C | |
| Injection Pressure | 3.00 - 55.0 | MPa | |
| Injection Rate | Moderate | ||
| Holding Pressure | 3.00 - 45.0 | MPa | |
| Back Pressure | 0.00 | MPa | |
| Cushion | 6.35 - 12.7 | mm |
| Injection instructions |
|---|
| Screw Speed: ModerateDecompression: 3.81 to 7.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA PP 2131 70/05 | MBA Polymers | PP Copolymer | MBA PP |
| RELENE® 46GP003 | Reliance Industries Limited | HDPE | RELENE® |
| WELLAMID Nylon 6600 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| HAIPLEN H30 G8 BA | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Hanwha Total PP HJ730L | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |