DOW™ LDPE PT 7007
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g7m0V3_DOW-LDPE-PT-7007.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW LDPE PT 7007 Polyethylene Resin is a low density polyethylene suitable designed for extrusion coating applications. DOW LDPE PT 7007 Polyethylene Resin has been designed to offer minimum volatile organic carbon (VOC) levels for use in extrusion coating, contributing to low factory emissions and optimal sensory performance. DOW LDPE PT 7007 Polyethylene Resin exhibits:
Note: DOW LDPE PT 7007 Polyethylene Resin should comply with U.S. FDA CFR 177.1520(c)2.2 and with EU, No 10/2011 when used unmodified and processed according to good manufacturing practices for food contact applications. Please contact your nearest office regarding food contact compliance statements. The purchaser remains responsible for determining whether the use complies with all relevant regulations. Applications:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 8.00 | MPa | |
| Break | 10.0 | MPa | |
| Tensile Strain (Break) | 400 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Seal Initiation Temperature 1 | 105 | °C | Internal Method |
| Water Vapor Transmission 2 | 260 | g/m²/24 hr | ASTM E398-83 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 89.0 | °C | ISO 306/A |
| Extrusion | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Temperature | 270 to 335 | °C | |
| Minimum Coating Weight 3 | 5.0 | g/m² | Internal Method |
| Neck-in | Internal Method | ||
| -- 4 | 65.0 | mm | |
| -- 5 | 75.0 | mm | |
| -- 6 | 70.0 | mm |
| Note Message | |
|---|---|
| 1 . | Temperature required to reach 3 N/15 mm for a 25 g/m² coating of LDPE PT 7007 Polyethylene Resin onto paper. |
| 2 . | 23°C, 90% RHDivide by coating weight in g/m² to obtain actual WVTR, e.g. at 20 g/m² LDPE PT 7007 Polyethylene Resin the WVTR is 378/20= 18.9 g/m² day |
| 3 . | At 320°C set temperature. |
| 4 . | 100 m/min, 25 g/m² coatings at 290°C set temperature. |
| 5 . | 300 m/min, 25 g/m² coatings at 290°C set temperature. |
| 6 . | 200 m/min, 25 g/m² coatings at 290°C set temperature. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michilar T7200GF30 | API Polymers, Inc. | PET | Michilar |
| Yanshan PE 1140A | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| ASTALAC™ ABS X13 | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |
| CENUSIL® R 140 | Wacker Chemie AG | Silicone | CENUSIL® |
| PALDUR® R 15 GF 20 | pal plast GmbH | PBT | PALDUR® |