Akulon® S223-EH
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g7krAG_Akulon-S223-EH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon® S223-EH is a Polyamide 66 (Nylon 66) material. It is available in Asia Pacific or Europe. Important attributes of Akulon® S223-EH are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.6 | -- | % | |
| Flow | 1.6 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 8.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.3 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3500 | 1500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 95.0 | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 3.5 | 20 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 25 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2800 | -- | MPa | ISO 178 |
| Flexural Stress | 125 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | 6.0 | kJ/m² | |
| 23°C | 6.0 | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 225 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.0E-4 | -- | cm/cm/°C | |
| Transverse | 1.0E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 25 | 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.40 | 10.0 | ||
| 1 MHz | 3.20 | 4.00 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.013 | 0.30 | ||
| 1 MHz | 0.020 | 0.10 | ||
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | V-2 | -- | ||
| 0.710 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 265 to 285 | °C | |
| Middle Temperature | 275 to 290 | °C | |
| Front Temperature | 280 to 295 | °C | |
| Nozzle Temperature | 280 to 290 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Milastomer™ 8030NHS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| TAROMID A 280 X0 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| TIPELIN® BS 501-17 | MOL Petrochemicals Co. Ltd. | HDPE | TIPELIN® |
| POLYFLON™ M-139 | Daikin Fluorochemicals (China) Co., Ltd. | PTFE | POLYFLON™ |
| LEXAN™ CFR9111 resin | SABIC Innovative Plastics | PC | LEXAN™ |