Adell Polyamide AF-10-667
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Adell Plastics, Inc. |
| Trademark: | Adell Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g7kPUq_Adell-Polyamide-AF-10-667.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Adell Polyamide AF-10-667 is a Polyamide 66 (Nylon 66) material. It is available in North America. Primary attribute of Adell Polyamide AF-10-667: Flame Retardant. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.70 to 1.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.0 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 65.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 4140 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 27 | J/m | ASTM D256 |
| Tensile Impact Strength | 84.1 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 218 | °C | |
| 1.8 MPa, Unannealed | 127 | °C | |
| Melting Temperature | 249 to 260 | °C | |
| RTI Elec (0.710 mm) | 130 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 0.710 mm | 75.0 | °C | |
| 1.47 mm | 85.0 | °C | |
| RTI Str | UL 746 | ||
| 0.710 mm | 120 | °C | |
| 1.47 mm | 130 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Arc Resistance (3.05 mm) | 60.0 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) (3.05 mm) | 212 | V | UL 746 |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 0.710 mm | 51.0 | ||
| 3.05 mm | 90.0 | ||
| High Voltage Arc Tracking Rate (HVTR) | UL 746 | ||
| 0.710 mm | 115 | mm/min | |
| 1.47 mm | 52.0 | mm/min | |
| Hot-wire Ignition (HWI) (0.710 mm) | 45 | sec | UL 746 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viprene™ P80A-22U-NAT | Alliance Polymers & Services | TPV | Viprene™ |
| ELASTOSIL® SOLAR 1109 WHITE | Wacker Chemie AG | Silicone | ELASTOSIL® SOLAR |
| SEQUEL® 1719HF-UV WHIT | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| PSM® HL-100B2F | Wuhan Huali Environmental Technology Co., Ltd. | TP, Unspecified | PSM® |
| Sylvin 9077-90LMW Grey 9167 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |