EXCELLOY AK12G20
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | Techno Polymer Co, Ltd. |
| Trademark: | EXCELLOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g7NsgA_EXCELLOY-AK12G20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EXCELLOY AK12G20 is an Acrylonitrile Butadiene Styrene + Nylon (ABS+Nylon) product filled with 20% glass fiber. It can be processed by injection molding and is available in Asia Pacific or North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.22 | -- | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (260°C/10.0 kg) | 38 | -- | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.10 to 0.40 | -- | % | ISO 294-4 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ||||
| R-Scale | 116 | 112 | ASTM D785 | |
| R-Scale | 115 | 111 | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ||||
| Yield | 103 | 89.2 | MPa | ASTM D638 |
| Yield | 97.0 | 82.0 | MPa | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 5100 | 3510 | MPa | ASTM D790 |
| -- | 4750 | 3390 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 157 | 118 | MPa | ASTM D790 |
| -- | 167 | 117 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 15 | 28 | kJ/m² | ISO 179 |
| Notched Izod Impact | 130 | 240 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 142 | 136 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 135 | 128 | °C | ISO 75-2/B |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Rear Temperature | 240 to 280 | °C | |
| Middle Temperature | 240 to 280 | °C | |
| Front Temperature | 240 to 280 | °C | |
| Mold Temperature | 50.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALFILL H 15 20 T0 | RIALTI Srl | PP Homopolymer | RIALFILL |
| Moplen HP493M | LyondellBasell Industries | PP Homopolymer | Moplen |
| Chemical Resources PP 2000NW | Chemical Resources, Inc. | PP Homopolymer | Chemical Resources |
| Devcon Titanium Putty | Devcon | Epoxy | Devcon |
| OTECH PVC OM6525-Boot | OTECH Corporation | PVC, Unspecified | OTECH PVC |