Badamid® UL A70 H
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g7KuoY_Badamid-UL-A70-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid®UL A70 H is a polyamide 66 (nylon 66) material,. This product is available in Europe,. Badamid®The main characteristics of UL A70 H are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 8.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.8 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3150 | 1600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 83.0 | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 4.5 | 21 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 15 | 50 | % | ISO 527-2/50 |
| Flexural Stress (23°C) | 135 | 65.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 3.0 | 3.0 | kJ/m² | ISO 180/1A |
| 23°C | 5.0 | 11 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1 | ||||
| 0.45 MPa, not annealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 75.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 262 | -- | °C | ISO 3146 |
| CLTE - Flow (4.00 mm) | 8.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength | 32 | 26 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.60 | 5.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.025 | 0.20 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-2 | -- | UL 94 | |
| 1.60 mm | V-2 | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Short-Term Heat Resistance, IEC 216, 20000 hrs: 200°CLong-Term Heat Resistance, IEC 216, 50% decrease of yield stress: 90°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 110x10x4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tekumid 6 BS | TEKUMA Kunststoff GmbH | Nylon 6 | Tekumid |
| Alcryn® 4060 BK | Advanced Polymer Alloys | MPR | Alcryn® |
| Elastollan® C 60 D | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Honeywell PCTFE P8000TR | Honeywell | PCTFE | Honeywell PCTFE |
| Jiangsu Sinarise JM8211 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |