RTP 2383 C
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g7HNWh_RTP-2383-C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Carbon Fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.010 - 0.14 | % | ASTM D955 |
| Moisture Content | 0.010 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12400 | MPa | ASTM D638 |
| Tensile Strength | 186 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.0 - 4.5 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 259 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 85 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 530 | J/m | ASTM D4812 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 132 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Dew Point | -40.0 | °C | |
| Processing (Melt) Temp | 238 - 260 | °C | |
| Mold Temperature | 93.3 - 121 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SNOLEN® EM 2.8/58 | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| Veroplas 660 | PlastxWorld Inc. | ABS | Veroplas |
| Forprene® 6NM001A85 | SO.F.TER. SPA | TPV | Forprene® |
| Iupilon® DH3002R | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| LONGLITE® LCP LCP-300 N3G | CCP Group | LCP | LONGLITE® LCP |