Category: | Fluorelastomer , Fluoroelastomer |
Manufacturer: | 3M Advanced Materials Division |
Trademark: | 3M™ Dyneon™ Fluoroelastomer |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | g7FaR4_3MDyneonFluoroelastomerFC2179.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
3M™ Dyneon™ Fluoroelastomer FC 2179 is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FC 2179 has an incorporated bisphenol cure system. Special Features
Typical Applications 3M™ Dyneon™ Fluoroelastomer FC 2179 is suitable for the manufacture of O-rings with very good compression set resistance. |
General Information | |
---|---|
Features |
|
Uses |
|
Appearance |
|
Forms |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.80 | g/cm³ | Internal method |
Mooney Viscosity (ML 1+10, 121°C) | 80 | MU | Internal method |
Fluorine Content | 66 | % | Internal method |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Durometer Hardness (Shore A) | 74 | ASTM D2240 |
Elastomers | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Stress 1(100% Strain) | 7.00 | MPa | ASTM D412A |
Tensile Strength 2 | 16.5 | MPa | ASTM D412A |
Tensile Elongation 3(Break) | 200 | % | ASTM D412A |
Compression Set | ASTM D1414 | ||
200°C, 70 hr 4 | 13 | % | ASTM D1414 |
200°C, 70 hr 5 | 10 | % | ASTM D1414 |
Note Message | |
---|---|
1 . | D mould |
2 . | Die D |
3 . | D mould |
4 . | Post cured 16 hours @ 230°C |
5 . | Post cured 24 hours @ 260°C |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Sylvin 2910-95 Clear | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
Xuchuan XCW-6650D | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
CERTENE™ PHM-5A | Muehlstein | PP Homopolymer | CERTENE™ |
HAIPLEN H10 G4 BA | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
HiFill® PC / PBT IM 5301 UV BK | Techmer Engineered Solutions | PC+PBT | HiFill® |