TPSiV™ 4000-50A
| Category: | TPSiV , Thermoplastic Silicone Vulcanizate |
| Manufacturer: | Multibase, A Dow Corning Company |
| Trademark: | TPSiV™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g72z8K_TPSiV-4000-50A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TPSiV® 4000-50A Thermoplastic Elastomer is a UV stable, colorable, thermoplastic elastomer with excellent bonding to Polycarbonate, ABS, and similar polar substrates. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/10.0 kg) | 56 | g/10 min | ISO 1133 |
| Molding Shrinkage | 2.0 to 4.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 15 sec) | 48 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 14.0 | MPa | ISO 178 |
| Flexural Stress | 0.740 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles) | 155 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 1.50 | MPa | ISO 37 |
| Tensile Stress (Yield) | 4.40 | MPa | ISO 37 |
| Tensile Elongation (Break) | 710 | % | ISO 37 |
| Tear Strength | 20 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 22 hr | 25 | % | |
| 70°C, 22 hr | 77 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 150 to 160 | °C | |
| Middle Temperature | 155 to 165 | °C | |
| Front Temperature | 160 to 170 | °C | |
| Nozzle Temperature | 170 to 190 | °C | |
| Processing (Melt) Temp | 180 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C | |
| Injection Rate | Moderate-Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RapidVac™ VA-1800 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| Iupiace® AP6GM4 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| Karina CLEAR PVC COMPOUND 65/213 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lutene® XL8080NTS | LG Chem Ltd. | PE, Unspecified | Lutene® |
| LEXAN™ XHT5146 resin | SABIC Innovative Plastics | PC | LEXAN™ |