Innothane® IE-72DC
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g6iv00_Innothane-IE-72DC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-72DC is a water-clear, rigid polyurethane formulated for room temperature hand-batch or vacuum assisted casting methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. The unique chemistry of IE-72DC imparts excellent optical clarity as well as U.V. stability. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.05 | g/cm³ | |
| Cured | 1.10 | g/cm³ | |
| Base Resin | 1.16 | g/cm³ | |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed 1 | 77.0 | °C | |
| 0.45 MPa, Unannealed | 60.0 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 55 Mix Ratio by Weight: 50 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 120 to 240 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Exotherm - 200g mass | 138 | °C |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 2 | 0.90 | Pa·s | |
| 25°C 3 | 1.2 | Pa·s | |
| 25°C 4 | 4.0 | Pa·s | |
| Curing Time (25°C) | 24 | hr | |
| Gel Time | 15 to 20 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 75 to 85 | ASTM D2240 | |
| Tensile Strength | 55.2 | MPa | ASTM D638 |
| Tensile Elongation at Break | 2.0 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | 8 hour @ 150°F post-cure |
| 2 . | Resin |
| 3 . | Mixed |
| 4 . | Hardener |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SE-110M68 | SHIN-A T&C | Epoxy | SHIN-A |
| SEPAZ™ K445GTS | Mando Advanced Materials Co., Ltd. | PPS | SEPAZ™ |
| Karina GRAY PVC COMPOUND 800-18/101-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1-8934/BL/L | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Sylvin 3270-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |