NEALID XW400H - 8229
| Category: | Nylon+Olefin , Polyamide + Polyolefin |
| Manufacturer: | AD majoris |
| Trademark: | NEALID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g6QZcp_NEALID-XW400H---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NEALID XW400H-8229 is a 40 % glass fibre/mineral reinforced polyamide alloy black intended for injection moulding. APPLICATIONS Products requiring excellent combination between thermal and mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6130 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 47.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 5000 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 24 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 161 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 121 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 245 to 265 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 255 to 275 | °C | |
| Nozzle Temperature | 255 to 275 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 D MS 5 | RTP Company | Nylon 612 | RTP |
| PRIME TPO E-2740 | Prime Polymer Co., Ltd. | PP Random Copolymer | PRIME TPO |
| SLOVALEN® PC 11 N | Plastcom | PP Copolymer | SLOVALEN® |
| Devlon Acetal Homopolymer | Devol® Engineering Polymers | Acetal (POM) Homopolymer | Devlon |
| Pibiter® N200 NAT001 | SO.F.TER. SPA | PBT | Pibiter® |