NANCAR® 3365
| Category: | NBR , Acrylonitrile Butadiene Rubber |
| Manufacturer: | Nantex Industry Co., Ltd. |
| Trademark: | NANCAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g6LNgy_NANCAR-3365.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NANCAR® 3365 is a medium high acrylonitrile butadiene copolymer with good oil resistance. It is polymerized at low temperature and contains sufficient antioxidant for normal aging conditions. It has superior processing characteristics, fast curing rate, low mold fouling and superior resilience properties. NANCAR® 3365 is an excellent multi-purpose nitrile elastomer. It may be blended with vinyl resins to produce smooth extrusions and nerve-free sheets. Suggested applications include those in fuel hoses, packings, gaskets, oil seals, other car parts, oil resistant belts, footwear and roll covers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.980 | g/cm³ | |
| Mooney Viscosity (ML 1+4, 100°C) | 62 | MU | ASTM D1646 |
| Acrylonitrile Content - Bound | 33.0 | % | Internal Method |
| Solubility - in MEK | 100 | % | |
| Stabilizer | Non-staining |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Loss | 0.20 | % | ASTM D5688 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A 1 | 73 | ||
| Shore A 2 | 72 | ||
| Shore A 3 | 71 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 300% Strain 4 | 9.32 | MPa | |
| 300% Strain 5 | 10.5 | MPa | |
| 300% Strain 6 | 11.4 | MPa | |
| Tensile Strength | ASTM D412 | ||
| Yield 7 | 27.8 | MPa | |
| Yield 8 | 27.0 | MPa | |
| Yield 9 | 27.3 | MPa | |
| Tensile Elongation | ASTM D412 | ||
| Break 10 | 620 | % | |
| Break 11 | 580 | % | |
| Break 12 | 560 | % | |
| Tear Strength | 56.9 | kN/m | ASTM D624 |
| Compression Set 13(100°C, 70 hr) | 55 | % | ASTM D395 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 14(100°C, 70 hr) | -14 | % | ASTM D865 |
| Change in Ultimate Elongation in Air 15(100°C, 70 hr) | -38 | % | ASTM D865 |
| Change in Durometer Hardness in Air 16(Shore A, 100°C, 70 hr) | 4.0 | ASTM D865 | |
| Change in Tensile Strength 17 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM #1 Oil | -11 | % | |
| 100°C, 70 hr, in ASTM #3 Oil | -28 | % | |
| Change in Ultimate Elongation 18 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM #1 Oil | -28 | % | |
| 100°C, 70 hr, in ASTM #3 Oil | -28 | % | |
| Change in Durometer Hardness 19 | ASTM D471 | ||
| Shore A, 100°C, 70 hr, in ASTM #1 Oil | 1.0 | ||
| Shore A, 100°C, 70 hr, in ASTM #3 Oil | -9.0 | ||
| Change in Volume 20 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM Oil #1 | 0.40 | % | |
| 100°C, 70 hr, in ASTM Oil #3 | 16 | % |
| Note Message | |
|---|---|
| 1 . | Cured for 60.0 min at 150°C |
| 2 . | Cured for 40.0 min at 150°C |
| 3 . | Cured for 20.0 min at 150°C |
| 4 . | Cured for 20.0 min at 150°C |
| 5 . | Cured for 40.0 min at 150°C |
| 6 . | Cured for 60.0 min at 150°C |
| 7 . | Cured for 60.0 min at 150°C |
| 8 . | Cured for 40.0 min at 150°C |
| 9 . | Cured for 20.0 min at 150°C |
| 10 . | Cured for 20.0 min at 150°C |
| 11 . | Cured for 40.0 min at 150°C |
| 12 . | Cured for 60.0 min at 150°C |
| 13 . | Cured for 60.0 min at 150°C |
| 14 . | Cured for 40.0 min at 150°C |
| 15 . | Cured for 40.0 min at 150°C |
| 16 . | Cured for 40.0 min at 150°C |
| 17 . | Cured for 40.0 min at 150°C |
| 18 . | Cured for 40.0 min at 150°C |
| 19 . | Cured for 40.0 min at 150°C |
| 20 . | Cured for 40.0 min at 150°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® FPP LGF 50 | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| PureTherm® 1001C White Opaque | Tekni-Films, a div of Tekni-Plex | Film, PVC | PureTherm® |
| D-MEC SCR751 | D-MEC Ltd. | Epoxy | D-MEC |
| Capilene® TP 50 AV | Carmel Olefins Ltd. | PP Impact Copolymer | Capilene® |
| Zytel® ST811HS BK038 | DuPont Performance Polymers | Nylon 6 | Zytel® |