LNP™ THERMOCOMP™ Lexan_LGK3020 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g6Ga9Z_LNPTHERMOCOMPLexanLGK3020compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP LEXAN_LGK3020 compound is a glass reinforced, flame retardant material. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.050 - 0.25 | % | Internal method |
| Transverse flow : 3.20mm | 0.15 - 0.35 | % | Internal method |
| Water Absorption (24 hr) | 0.13 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 118 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 6580 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 50.0 mm Span) | 148 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 146 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 30°C | 2.7E-5 | cm/cm/°C | ASTM D696 |
| Lateral : -30 to 30°C | 4.7E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.20 mm, in Oil) | 18 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 293 - 316 | °C | |
| Middle Temperature | 304 - 327 | °C | |
| Front Temperature | 316 - 338 | °C | |
| Nozzle Temperature | 310 - 332 | °C | |
| Processing (Melt) Temp | 316 - 338 | °C | |
| Mold Temperature | 82.2 - 116 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vital-Line SHM2532G4 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Advanced-PP 1104H | Advanced Petrochemical Company | PP Homopolymer | Advanced-PP |
| ARCEL® LD (1.5 pcf) | NOVA Chemicals | PS+PE | ARCEL® |
| Sylvin 6177-80 Orange 5111 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| MARPOL® HDB 546 | Marco Polo International, Inc. | HDPE | MARPOL® |