INTEGRAL™ 848

Category:	Polyolefin, Unspecified , Polyolefin Adhesive Film
Manufacturer:	The Dow Chemical Company
Trademark:	INTEGRAL™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	g5bLzM_INTEGRAL-848.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
INTEGRAL™ 848 Film is a multi-layer adhesive film. One layer provides high flow adhesives, great for adhering to porous substrates such as non-wovens, natural fibers, and polyurethane foams, while the second layer provides barrier properties. New experimental films are continually being developed. Please discuss your particular application needs with your Dow representative. General Characteristics: Heat Activation Point: 215°F (102°C) Yield: 204 sq ft/lb/mil (41.8 m²/kg/25 µm) Available Colors: Black, Red, and Blue Gauge Range: Black: 0.75, 0.85, and 1.0 mil (19, 21, and 25 µm); Red, Blue: 1.0-3.0 mil (25-75 µm) Width Range: 20-75 in (508-1905 mm)

Message

INTEGRAL™ 848 Film is a multi-layer adhesive film. One layer provides high flow adhesives, great for adhering to porous substrates such as non-wovens, natural fibers, and polyurethane foams, while the second layer provides barrier properties.

New experimental films are continually being developed. Please discuss your particular application needs with your Dow representative.

General Characteristics:

Heat Activation Point: 215°F (102°C)

Yield: 204 sq ft/lb/mil (41.8 m²/kg/25 µm)

Available Colors: Black, Red, and Blue

Gauge Range: Black: 0.75, 0.85, and 1.0 mil (19, 21, and 25 µm); Red, Blue: 1.0-3.0 mil (25-75 µm)

Width Range: 20-75 in (508-1905 mm)

General Information
Appearance	Black Blue Red
Forms	Film

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	51	µm
Film Thickness - Recommended / Available	Black: 0.75; 0.85; 1.0 mil (19; 21; 25 µ) Red, Blue: 1.0-3.0 mil (25-75 µ)
Secant Modulus			ASTM D882
2% Secant, MD : 51 µm	174	MPa
2% Secant, TD : 51 µm	201	MPa
Tensile Strength			ASTM D882
MD : Break, 51 µm	22.0	MPa
TD : Break, 51 µm	16.3	MPa
Tensile Elongation			ASTM D882
MD : Break, 51 µm	420	%
TD : Break, 51 µm	520	%
Elmendorf Tear Strength			ASTM D1922
MD : 51 µm	88	g
TD : 51 µm	600	g
Film Width	50.80 to 190.50	cm
Yield (25.4 µm)	42.7	m²/kg

Thermal	Nominal Value	Unit
Heat Activation Temperature	102	°C

Resin Grade	Manufacturer	Category	Trademark
RTP 300 AR 10 TFE 10	RTP Company	PC	RTP
Spartech Polycom MG5519LT-2	Spartech Polycom	PVC Alloy	Spartech
Geon™ Vinyl Flexible XV3860	PolyOne Corporation	PVC, Flexible	Geon™ Vinyl Flexible
LNP™ THERMOCOMP™ RF004 compound	SABIC Innovative Plastics	Nylon 66	LNP™ THERMOCOMP™
CERTENE™ PBM-35	Muehlstein	PP Impact Copolymer	CERTENE™