ACRYLITE® Film 0F063
| Category: | Film, PMMA , PMMA Film |
| Manufacturer: | Evonik Cyro LLC |
| Trademark: | ACRYLITE® Film |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g54u5C_ACRYLITE-Film-0F063.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ACRYLITE® Film 0F063 is a very high weather resistant and transparent acrylic film for graphic printings and lamination systems. Due to its excellent performance under weathering and UV light exposure, ACRYLITE® Film 0F063 does not present color change or yellowing. Therefore it provides high protection of polymeric substrates from degradation caused by UV radiation. Its very smooth surface leads the film to have a good optical quality surface. Application ACRYLITE® Film 0F063 is suitable as top layer for high UV and weathering protection of different polymeric substrates including ones based on Fiber Reinforced Polyester Resin. ACRYLITE® Film 0F063 can be used to be printed on as good quality film decoration and then laminated on different polymeric films or sheets. Laminated decoration films based on ACRYLITE® are suitable for a wide range of molding processes such as thermoforming and insert molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | DIN 53479 |
| Surface Tension | 50 | mN/m | DIN 53364 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| UV Transmittance - 280 - 380 nm | < 1.0 | % | DIN EN 410 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Accelerated Weathering Resistance - method A, cycle 1, 65% RH 1 | No Visible Change | ISO 4892-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 62.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| Yield | 7.0 | % | |
| Break | 21 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 114 | °C | ISO 11357-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ISO 489 | |
| Transmittance 2 | 92.0 | % | ISO 13468-2 |
| Note Message | |
|---|---|
| 1 . | 8,000 hr |
| 2 . | D65 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN V-235N | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| Radilon® S RV500 | Radici Plastics | Nylon 6 | Radilon® |
| TYLON® 2413 | Tyne Plastics LLC. | Nylon 6 | TYLON® |
| Kostrate® EDGE UT | Plastic Selection Group, Inc. | TP, Unspecified | Kostrate® EDGE |
| Lucon® CP6054 | LG Chem Ltd. | PC | Lucon® |