Ravamid® BGF40 BK45
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Ravago Group |
| Trademark: | Ravamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g4z1Fi_Ravamid-BGF40-BK45.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Black, 40% glass fibre reinforced, general purpose All the products are also available Heat Stabilized (H) and UV Stabilized (UV) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 0.16 to 0.85 | % | ASTM D955 |
| Humidity | < 0.15 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9800 | MPa | ASTM D882, ISO 527-2 |
| Tensile Strength (Break) | 165 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 8900 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 60 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (Area) (23°C) | 9.50 | kJ/m² | ASTM D256 |
| Notched Izod Impact Strength (23°C) | 9.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 220 | °C | ISO 306/B50, ASTM D1525 1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (3.20 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC V142-70 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Trademark PE LLB1918B | Trademark Plastics Corporation | LLDPE | Trademark PE |
| Ultraform® FK 66003 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| EPO-TEK® OG146-104 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| PLANAC BT-3500 | TOYOBO America, Inc. | PBT | PLANAC |