VIBRATHANE 8030 is an MDI terminated, polycaprolactone based prepolymer that is solid at room temperature. This high performance material yields an 80A durometer urethane when cured with 1,4-Butanediol. It was designed for applications such as wiper blades. VIBRATHANE 8030 elastomers are characterized by:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 4.83 | MPa | ASTM D412 |
| Tensile Strength | 33.1 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 300 | % | ASTM D412 |
| Tear Strength (Split) | 21 | kN/m | ASTM D470 |
| Compression Set (70°C, 22 hr) | 29 | % | ASTM D395B |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 5.0 | min | |
| Post Cure Time (115°C) | 16 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Curing Time (115°C) | 0.50 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 225H | RTP Company | Nylon 66 | RTP |
| Tenac™ GA520 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| NIMA NH PC143P | Ovation Polymers Inc. | PC | NIMA |
| ALCOM® PA6 900/13 GF15 MRX45 | ALBIS PLASTIC GmbH | Nylon 6 | ALCOM® PA6 |
| APEX® 07-U0296A-65 | Teknor Apex Company | PVC, Flexible | APEX® |