Borcom™ WE007AE
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borcom™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g4qqBs_Borcom-WE007AE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Borcom WE007AE is a polypropylene microcomposite intended for injection moulding. The product is available in natural colour. This material has an excellent balance between impact strength and stiffness and gives a good surface quality. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/10) | 36.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 7.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1250 | MPa | ISO 178 |
| Flexural Stress | 25.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.7 | kJ/m² | ISO 179/1eA |
| -20°C | 5.5 | kJ/m² | ISO 179/1eA |
| 23°C | 35 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 150 | kJ/m² | ISO 179/1eU |
| 23°C | 170 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C | 5.0 | kJ/m² | ISO 180/1A |
| 23°C | 30 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 89.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 134 | °C | ISO 306/A50 |
| -- | 47.0 | °C | ISO 306/B50 |
| CLTE - Flow (-30 to 80°C) | 6.5E-5 | cm/cm/°C | Internal method |
| Melt Energy | 80.0 | kJ/kg | ISO 11357 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 - 280 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperature: 40 to 80°CBack pressure: low to mediumScrew speed: low to mediumFlow front speed: 100 to 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® R513H | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| TYLON® 1413 | Tyne Plastics LLC. | Nylon 66 | TYLON® |
| Braskem PP CP 204 | Braskem | PP Copolymer | Braskem PP |
| LNP™ THERMOCOMP™ EF004 compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |
| Sumiliteresin® PR-53056 | SBHPP | Phenolic | Sumiliteresin® |