WONDERLITE® PC-175
| Category: | PC , Polycarbonate |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | WONDERLITE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g4W70y_WONDERLITE-PC-175.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| WONDERLITE® PC-175 is a Polycarbonate (PC) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Electrical/Electronic Applications. Primary characteristic: rohs compliant. |
| General Information | |
|---|---|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 62 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 65.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 to 0.70 | % | |
| Across Flow | 0.50 to 0.70 | % | |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 77 | ASTM D785 | |
| Ball Indentation Hardness (H 358/30) | 106 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 3.18 mm 1 | 63.7 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Break | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield, 3.18 mm 2 | 6.0 | % | ASTM D638 |
| Break, 3.18 mm 3 | 70 | % | ASTM D638 |
| Break | 65 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 6.35 mm 4 | 2350 | MPa | ASTM D790 |
| -- 5 | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| 6.35 mm 6 | 90.2 | MPa | ASTM D790 |
| -- 7 | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | ||
| 1.8 MPa, Unannealed | 124 | °C | |
| 1.8 MPa, Annealed | 140 | °C | |
| Vicat Softening Temperature | |||
| -- | 145 | °C | ISO 306/A50 |
| -- | 140 | °C | ISO 306/B50 |
| CLTE - Flow (44 to 100°C) | 6.0E-5 to 8.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.0E+16 | ohms·cm | ASTM D257 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.585 | ASTM D542 | |
| Transmittance (76200 µm) | 89.0 | % | ASTM D1003 |
| Haze (81300 µm) | < 0.80 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 290 to 320 | °C | |
| Middle Temperature | 310 to 385 | °C | |
| Front Temperature | 270 to 350 | °C | |
| Mold Temperature | 45.0 to 128 | °C |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 6.0 mm/min |
| 3 . | 6.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nylene® 132-250 HS | Custom Resins Group | Nylon 66 | Nylene® |
| Celanex® 3216HR | Celanese Corporation | PBT | Celanex® |
| ELASTOSIL® RT 646 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® RT |
| Infino CF-1051 | SAMSUNG SDI CO., LTD. | PC | Infino |
| AvaSpire® AV-481 | Solvay Specialty Polymers | PAEK | AvaSpire® |