ACRYLITE® Hi-Gloss NTA-1

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Cyro LLC
Trademark:	ACRYLITE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	g48Qs6_ACRYLITE-Hi-Gloss-NTA-1.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

ACRYLITE® Hi-Gloss NTA-1 polymer is an opaque, amorphous, and impact-modified thermoplastic molding and extrusion compound based on polymethyl methacrylate.

Typical properties of ACRYLITE® Hi-Gloss acrylic polymers are:

excellent weather resistance

improved resistance to stress cracking

good melt flow rate

good polishability

impact resistance

The special properties of ACRYLITE® Hi-Gloss NTA-1 polymer are:

good heat resistance

available in a range of opaque colors

high melt strength

increased impact/break resistance and strength

Application:
Used for injection molding technical parts.

General Information
Additive	Impact Modifier
Features	Amorphous Good Flow Good Impact Resistance Good Melt Strength Good Strength Good Weather Resistance Impact Modified Medium Heat Resistance
Uses	Automotive Applications Automotive Exterior Trim Automotive Interior Trim Housings
Agency Ratings	EC 1907/2006 (REACH)
Appearance	Colors Available Opaque
Forms	Pellets
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.18	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	3.00	cm³/10min	ISO 1133
Water Absorption (Equilibrium, 23°C, 50% RH)	< 3.0	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2700	MPa	ISO 527-2/1
Tensile Stress (Yield)	68.0	MPa	ISO 527-2/50
Tensile Strain (Yield)	5.0	%	ISO 527-2/50
Nominal Tensile Strain at Break	10	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	33	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	103	°C	ISO 75-2/B
1.8 MPa, Unannealed	102	°C	ISO 75-2/A
Glass Transition Temperature	120	°C	IEC 1006
Vicat Softening Temperature	110	°C	ISO 306/B50

Flammability	Nominal Value	Unit	Test Method
Glow Wire Ignition Temperature	675	°C	IEC 60695-2-13
Fire Rating	B2		DIN 4102

Resin Grade	Manufacturer	Category	Trademark
SUPREME HIPS SH 810HF	Supreme Petrochem Ltd.	PS (HIPS)	SUPREME HIPS
Nypol® PA A3 G50 HS NTLA013 NR356	Petropol Industry and Trade of Polymers LTDA	Nylon 66	Nypol® PA
Ad-Tech Urethanes UC-4750-1	Ad-Tech Plastic Systems Corp.	TSU	Ad-Tech Urethanes
FM® 6555-1	Cytec Industries Inc.	Adhesive	FM®
Starflam SF0067	Eurostar Engineering Plastics	Nylon 12	Starflam