Andur 9000 AP/Curene® 442
| Category: | PUR-Ether/TDI , Polyurethane (Polyether, TDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g46mGl_Andur-9000-AP-Curene-442.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur 9000-AP is a polyether (PPG) based liquid, toluene diisocyanate terminated prepolymer. An elastomer with a hardness of 90 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by reaction with various polyols and their combination with Curene 442 and other diamines, or through the use of plasticizers. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ASTM D1505 |
| Molding Shrinkage - Flow | 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 5% strain | 0.531 | MPa | ASTM D695 |
| 10% strain | 2.09 | MPa | ASTM D695 |
| 15% strain | 3.72 | MPa | ASTM D695 |
| 25% strain | 5.93 | MPa | ASTM D695 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 8.24 | MPa | ASTM D412 |
| 300% strain | 20.3 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 27.8 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 350 | % | ASTM D412 |
| Compression Set | 32 | % | ASTM D395B |
| Bayshore Resilience | 30 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 3.0 - 5.0 | min | |
| Demold Time | 30 - 45 | min | |
| Post Cure Time (96°C) | 16 | hr |
| Additional Information |
|---|
| Durometer Hardness, ASTM D2240, Shore A: 88 to 92Die C Tear, ASTM D1004: 322 pliAverage Split Tear, ASTM D1938: 102 pliStoichiometry Curative Level: 95%Mix Temperature: Andur 9000 AP: 180-212°F Curene 442: 235-250°F |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 104 - 113 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Formolene FORMAX® L91507E2 | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene FORMAX® |
| ELASTOSIL® R plus 4806/20 | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| ENFLEX V1070A BLK UV | ENPLAST Americas, a Ravago Group Company | TPV | ENFLEX |
| EPO-TEK® B9021-13 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| LNP™ THERMOCOMP™ RF006XXY compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |