| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Razin™ Engineering Plastics |
| Trademark: | Razamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g3wuR0_Razamid-A121U-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Razamid A121U-50 is an Injection grade Impact modified black color polyamide 66. It combines good strength, stiffness and toughness as well as excellent heat, chemical and abrasion resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 55.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 1900 | MPa | ASTM D790 |
| Flexural Strength | 75.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) (23°C) | 60.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 215 | °C | |
| 1.8 MPa, Unannealed | 80.0 | °C | |
| Vicat Softening Temperature | 225 | °C | ASTM D1525 |
| Peak Melting Temperature | 250 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 265 to 300 | °C | |
| Front Temperature | 275 to 305 | °C | |
| Processing (Melt) Temp | 275 to 310 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 55.0 to 140 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™ FS410 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| TAIRIPRO T1202 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| Galloo GP-PP-1065 | Galloo Plastics | PP, Unspecified | Galloo |
| Hyundai EP Adhesives LE200T/1002 | HYUNDAI EP Co., Ltd. | PE, Unspecified | Hyundai EP Adhesives |
| Axiall PVC 6335 Clear 125 | Axiall Corporation | PVC, Rigid | Axiall PVC |