RTP 199 X 143528
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g3UQd6_RTP199X143528.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ESD Protection - Permanently Static Dissipative - Flame Retardant - Preliminary Datasheet |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.0 - 1.5 | % | ASTM D955 |
| Moisture Content | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay 1 | sec | FTMS 101C 4046.1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ignition Resistance - Aerospace Value (3.18 mm) | 2.00 | FAR 25.853 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1380 | MPa | ASTM D638 |
| Tensile Strength | 22.1 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 1520 | MPa | ASTM D790 |
| Flexural Strength | 34.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 530 | J/m | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 - 9.9E+11 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+9 - 9.9E+10 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.0 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 191 - 232 | °C | |
| Mold Temperature | 32 - 66 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Do not exceed 520 °F (270 °C) melt temperature.Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | MIL-PRF-81705D, 5kV to 50 V, 12% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Modified Plastics MPP-S1 | Modified Plastics, Inc. | PP, Unspecified | Modified Plastics |
| Clariant Acetal CP-MF9 | Clariant Corporation | Acetal (POM) Copolymer | Clariant Acetal |
| KOPA® KN333G25CRBK | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Karina BLACK PVC COMPOUND -E TR-652D48/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SABIC® PPcompound 8250U | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |