IROGRAN® A 92 E 4860
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g3RVBb_IROGRAN-A-92-E-4860.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A92E 4860 is a high performance polyester based thermoplastic polyurethane intended for extrusion and injection moulding applications. IROGRAN A92E 4860 is part of the HUNTSMAN technical extrusion product range and offers a specially designed, flexible material with a broad processing window particularly suitable for the preparation of spiral tubing, pneumatic tubing, belting and technical mouldings. PERFORMANCE FEATURES
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.20 | g/cm³ | ASTM D792, DIN 53479 |
| Melt Volume-Flow Rate (MVR) (210°C/10.0 kg) | 33.0 | cm³/10min | |
| Molding Shrinkage - Flow (Injection Molded) | 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, DIN 53505 | ||
| Shore A, Injection Molded | 91 | ||
| Shore D, Injection Molded | 42 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | 25 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| TMA 3 | Internal Method | ||
| Low-High : 635.0 µm | 180 to 200 | °C | |
| Peak : 635.0 µm | 170 | °C |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 4 | |||
| 100% Strain | 8.00 | MPa | ASTM D412 |
| 100% Strain | 7.50 | MPa | DIN 53504 |
| 300% Strain | 15.2 | MPa | ASTM D412 |
| 300% Strain | 16.0 | MPa | DIN 53504 |
| Tensile Strength 5 | |||
| Break | 44.8 | MPa | ASTM D412 |
| Break | 49.0 | MPa | DIN 53504 |
| Tensile Elongation 6 | |||
| Break | 620 | % | ASTM D412 |
| Break | 590 | % | DIN 53504 |
| Tear Strength 7 | |||
| -- | 116 | kN/m | ASTM D624 |
| -- | 85 | kN/m | ISO 34-1 |
| Compression Set 8 | ASTM D395, ISO 815 | ||
| 23°C, 24 hr | 25 | % | |
| 70°C, 24 hr | 29 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Hot Air Dryer | 80.0 to 90.0 | °C | |
| Drying Time | |||
| -- | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Dew Point | -30.0 | °C | |
| Rear Temperature | 190 to 220 | °C | |
| Middle Temperature | 190 to 220 | °C | |
| Front Temperature | 190 to 220 | °C | |
| Nozzle Temperature | 210 to 225 | °C | |
| Processing (Melt) Temp | 205 to 220 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 25.0 to 40.0 | °C | |
| Cylinder Zone 1 Temp. | 200 to 210 | °C | |
| Cylinder Zone 2 Temp. | 200 to 210 | °C | |
| Cylinder Zone 3 Temp. | 200 to 210 | °C | |
| Cylinder Zone 4 Temp. | 200 to 210 | °C | |
| Cylinder Zone 5 Temp. | 200 to 210 | °C | |
| Adapter Temperature | 200 to 210 | °C | |
| Die Temperature | 200 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Extruded Film |
| 4 . | Injection Molded |
| 5 . | Injection Molded |
| 6 . | Injection Molded |
| 7 . | Injection Molded |
| 8 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® B3 GM 15/15 natural (3079) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| BONDYRAM® 7003 | Polyram Ram-On Industries | MAH-g | BONDYRAM® |
| LNP™ STAT-LOY™ A30009 compound | SABIC Innovative Plastics | ABS | LNP™ STAT-LOY™ |
| LONGLITE® PET 9130-200 | CCP Group | PET | LONGLITE® PET |
| Perfactory® E-Shell 300 | EnvisionTEC, Inc. | Acrylic, Unspecified | Perfactory® |