VAMPLEN 0024 V2 LBC
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g3Lwdg_VAMPLEN-0024-V2-LBC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UL 94 V2 at 1,6 mm, homopolymer, halogen free, good dimensional stability and thermal resistance, GWIT 775/1-2, RoHS. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.2 | % | |
| Across Flow | 1.2 | % | |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 100 | % | ASTM D638 |
| Flexural Modulus | 1900 | MPa | ASTM D790 |
| Flexural Strength | 35.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 2.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 25 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 70.0 | °C | ASTM D648A |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 1 |
| RTI Elec | 110 | °C | UL 746 |
| RTI Imp | 110 | °C | UL 746 |
| RTI Str | 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Glow Wire Flammability Index (1.00 to 2.00 mm) | 850 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 to 2.00 mm) | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 | °C | |
| Mold Temperature | 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4935 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| PONACOM PS 5360 | Ponachem Compound GmbH | PS (HIPS) | PONACOM PS |
| Precision Polymer V76F | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| NEFTEKHIM PS 625 | Nizhnekamskneftekhim Inc. | PS (HIPS) | NEFTEKHIM PS |
| Sylvin 6177-80 Red 6296 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |