Order Products : sales@su-jiao.com
Fortron® 0205B4/20µm
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g3GGRO_Fortron-0205B4-20-m.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Based on the adjusted particle size distribution, Fortron 0205B4/20¦m is suitable for coating processes. Chemical and physical properties (exception is the particle size distribution) are the same like for Fortron 0205B4. |
| General Information | |
|---|---|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ISO 527-2/1A/1 |
| Flexural Modulus (23°C) | 3900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 130 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 115 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 90.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 280 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 1.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 290 - 295 | °C | |
| Middle Temperature | 290 - 300 | °C | |
| Front Temperature | 300 - 310 | °C | |
| Nozzle Temperature | 300 - 310 | °C | |
| Processing (Melt) Temp | 295 - 330 | °C |
| Injection instructions |
|---|
| Feed Temperature: 285 to 290°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP VLF 80211 EM HS | RTP Company | Nylon 66 | RTP |
| TOTAL Polyethylene HDPE 2285 | TOTAL Refining & Chemicals | HDPE, HMW | TOTAL Polyethylene |
| XENOY™ HX6600HP resin | SABIC Innovative Plastics Europe | PC+PBT | XENOY™ |
| Formolene® 3355O | Formosa Plastics Corporation, U.S.A. | PP Random Copolymer | Formolene® |
| KOPLA PA66 KDT1020 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |