PRL PPX/NY-GP2
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g31hcn_PRL-PPX-NY-GP2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PPX/NY-GP2 is a Polyphenylene Ether + PS + Nylon (PPE+PS+Nylon) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/3.8 kg) | 10 to 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18 mm | 1.0 to 1.3 | % | |
| Across Flow : 3.18 mm | 0.90 to 1.2 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 57.9 | MPa | |
| Break, 3.18 mm | 55.2 | MPa | |
| Tensile Elongation (Break, 3.18 mm) | 50 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 2210 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.18 mm | 110 | J/m | |
| 23°C, 3.18 mm | 190 | J/m | |
| Gardner Impact (3.18 mm) | 28.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 154 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 129 | °C | |
| Vicat Softening Temperature | 199 | °C | ASTM D1525 1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 to 107 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 266 to 302 | °C | |
| Middle Temperature | 271 to 302 | °C | |
| Front Temperature | 279 to 302 | °C | |
| Processing (Melt) Temp | 279 to 302 | °C | |
| Mold Temperature | 76.7 to 121 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer N93H | Precision Polymer Engineering Ltd. | NBR | Precision Polymer |
| Staramide BG6ST01 | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| HANWHA CLNB-8141S | Hanwha Chemical | LDPE | HANWHA |
| E-RIALFILL H 07 20 T2 | RIALTI Srl | PP Homopolymer | E-RIALFILL |
| Lifoflex® UV FLAM 60600 | Müller Kunststoffe GmbH | TPE | Lifoflex® |