Bio-Flex® F 2201 CL
| Category: | PLA , Polylactic Acid |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Bio-Flex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g2U7DH_Bio-Flex-F-2201-CL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Biodegradable compound for film extrusion |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 - 10 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 7.00 - 9.50 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1150 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 27.0 | MPa | ISO 527-2 |
| Flexural Modulus | 1050 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 28.0 | MPa | ISO 178 |
| Tensile Strain at Tensile Strength | > 400 | % | ISO 527 |
| Flexural Strain at Break | No Break | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 145 - 160 | °C | ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.30 | % | |
| Cylinder Zone 1 Temp. | 160 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 175 | °C | |
| Cylinder Zone 4 Temp. | 180 | °C | |
| Adapter Temperature | 180 | °C | |
| Melt Temperature | < 190 | °C | |
| Die Temperature | 170 - 180 | °C |
| Extrusion instructions |
|---|
| Water jacket (feed): 35 °CDie gap: 0.8 - 1.4 mmDie diameter: up to 400 mmBlow film ratio: 2.5 - 4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RANPELEN SFC-750D | Lotte Chemical Corporation | PP Terpolymer | RANPELEN |
| XANTAR® MX 1001 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Formolene® 2610A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| LAPEROS® A410 | Polyplastics Co., Ltd. | LCP | LAPEROS® |
| Plaskon ALP-2 (197) | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |