Garathane™ X 96-322-A NAT
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | AlphaGary |
| Trademark: | Garathane™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g2TYNZ_Garathane-X-96-322-A-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GARATHANE X 96-322-A IS A PVC ALLOY FOOTWEAR COMPOUND |
| General Information | |
|---|---|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 to 1.22 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 67 to 73 | ||
| Shore A, 15 sec | 57 to 63 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance | |||
| loss, 1000 cycles | 0.350 | % | |
| loss, 5000 cycles | 2 | % | |
| Ross Flex (-29°C, 6.35 mm) | 30000 | ASTM D1052 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain, 1.91 mm) | 3.03 | MPa | ASTM D412 |
| Tensile Strength (1.91 mm) | 9.65 | MPa | ASTM D412 |
| Tensile Elongation (Break, 1.91 mm) | 400 | % | ASTM D412 |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Change in Volume 1 | |||
| 23°C, 168 hr, in Gasoline | -26 | % | |
| 23°C, 336 hr, in Gasoline | -26 | % | |
| 23°C, 336 hr, in Vegetable Oil | -22 | % | |
| 75°C, 168 hr, in Vegetable Oil | -28 | % |
| Note Message | |
|---|---|
| 1 . | Thickness: 75 mil |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4005 FR A L | RTP Company | PPA | RTP |
| Versaflex™ OM 2262 | PolyOne Corporation | TPE | Versaflex™ |
| LUBEMID B27 NATURAL UV | LUBEN PLAST srl | Nylon 6 | LUBEMID |
| Plaskon CMU-880-MA | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |
| Delene 5598 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |