CABELEC® XS6115
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Cabot Corporation |
| Trademark: | CABELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g2QG6s_CABELEC-XS6115.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CABELEC® XS6115 is a conductive compound based on conductive carbon black and glass fibre dispersed in a modified high density polyethylene resin. Its electrical and mechanical properties are permanent and are not dependent on atmospheric conditions. CABELEC® XS6115 is designed for injection moulding applications. It is recommended for product handling applications where freedom from the hazard of electrostatic discharge is necessary, such as handling of explosive powders and liquids, pigments or electronic components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.22 | g/cm³ | Internal Method |
| Melt Mass-Flow Rate (MFR) 2 | ISO 1133 | ||
| 190°C/10.0 kg | 2.0 | g/10 min | |
| 190°C/21.6 kg | 11 | g/10 min | |
| Molding Shrinkage - Flow 3 | 0.20 to 0.30 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 4(Shore D, 15 sec) | 66 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 5 | ISO 527-2 | ||
| Yield | 39.0 | MPa | |
| Break | 36.0 | MPa | |
| Tensile Strain 6(Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus 7 | 2790 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 8(23°C) | 13 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 9(1.8 MPa, Unannealed) | 92.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature 10 | 120 | °C | ISO 306/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 11 | 1.5E+2 | ohms | Internal Method |
| Volume Resistivity 12 | 24 | ohms·cm | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 225 | °C | |
| Middle Temperature | 225 | °C | |
| Front Temperature | 225 | °C | |
| Nozzle Temperature | 255 | °C | |
| Mold Temperature | 45.0 | °C |
| Note Message | |
|---|---|
| 1 . | CTM E023 |
| 2 . | CTM E005 |
| 3 . | CTM E047 |
| 4 . | CTM E030 |
| 5 . | CTM E041 |
| 6 . | CTM E041 |
| 7 . | CTM E040A |
| 8 . | CTM E044A |
| 9 . | CTM E038 |
| 10 . | CTM E039 |
| 11 . | CTM E042E |
| 12 . | CTM E043B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 383 TFE 5 SE | RTP Company | PC | RTP |
| QAMAR FD21HN | SPDC Ltd. | LLDPE | QAMAR |
| Anjacom® R100 | Almaak International GmbH | PC | Anjacom® |
| Evermore PUR SS-1023M | Evermore Chemical Industry Co., Ltd. | PUR-Ester | Evermore PUR |
| Karina BLACK PVC COMPOUND 808D48/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |