Static Dissipative Polycarbonate Features:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 44.1 | MPa | ASTM D638 |
| Fracture | 35.9 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 20 | % | ASTM D638 |
| Fracture | > 100 | % | ASTM D638 |
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| Flexural Strength | 600 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 530 - 640 | J/m | ASTM D256 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+8 - 1.0E+11 | ohms | ASTM D257 |
| Static Decay | sec | NFPA 99 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 121 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 221 - 232 | °C | |
| Middle Temperature | 227 - 238 | °C | |
| Front Temperature | 232 - 243 | °C | |
| Nozzle Temperature | 232 - 243 | °C | |
| Processing (Melt) Temp | 232 - 243 | °C | |
| Mold Temperature | 37.8 - 82.2 | °C | |
| Injection Pressure | 34.5 - 82.7 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Clamp Tonnage | 4.1 - 6.9 | kN/cm² |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 121 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Cylinder Zone 1 Temp. | 221 - 232 | °C | |
| Cylinder Zone 3 Temp. | 227 - 238 | °C | |
| Cylinder Zone 5 Temp. | 232 - 243 | °C | |
| Melt Temperature | 232 - 243 | °C | |
| Die Temperature | 232 - 243 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 25 to 100 RPM |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Rite® S408 | Lubrizol Advanced Materials, Inc. | Polyolefin, Unspecified | Stat-Rite® |
| WPP PP M 2097-004 | Washington Penn Plastic Co. Inc. | PP Impact Copolymer | WPP PP |
| IROGRAN® A 95 E 4813 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| Iupital® FX-11J | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| Karina IVORY PVC COMPOUND -E 75901-35/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |