Celanex® 2002
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g22zwU_Celanex-2002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex 2002 is a general purpose, unreinforced polybutylene terephthalate with a good balance of mechanical properties and processability. Celanex 2002 ia a medium flow material. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 20 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.8 - 2.0 | % | ASTM D955 |
| Vertical flow direction | 1.8 - 2.0 | % | ISO 294-4 |
| Flow direction | 1.8 - 2.0 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.19 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 78 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -40°C | 3100 | MPa | ASTM D638 |
| 23°C | 3170 | MPa | ASTM D638 |
| 80°C | 469 | MPa | ASTM D638 |
| 121°C | 296 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, -40°C | 101 | MPa | ASTM D638 |
| Yield, 0°C | 75.8 | MPa | ASTM D638 |
| Yield, 23°C | 55.8 | MPa | ASTM D638 |
| Yield, 80°C | 24.8 | MPa | ASTM D638 |
| Yield, 121°C | 17.9 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/1A/50 |
| Fracture | 35.0 | MPa | ISO 527-2/1A/50 |
| 50% strain | 30.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield, -40°C | 7.2 | % | ASTM D638 |
| Yield, 0°C | 4.4 | % | ASTM D638 |
| Yield, 23°C | 3.2 | % | ASTM D638 |
| Yield, 80°C | 17 | % | ASTM D638 |
| Yield, 121°C | 23 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/1A/50 |
| Fracture, 23°C | 200 | % | ASTM D638 |
| Fracture | 220 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 190 | kJ/m² | ISO 179/1eU |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact (23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 160 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 | °C | ASTM D648, ISO 75-2/A |
| Glass Transition Temperature | 60.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 190 | °C | ISO 306/B50 |
| Melting Temperature | 225 | °C | ISO 11357-3, ASTM D3418 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.4E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 1.0E+16 | ohms·cm | ASTM D257 |
| -- | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| -- 1 | 17 | kV/mm | ASTM D149 |
| -- | 23 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 MHz | 3.20 | ASTM D150 | |
| 100 Hz | 4.00 | IEC 60250 | |
| 1 MHz | 3.50 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.4E-3 | IEC 60250 | |
| 1 MHz | 0.022 | IEC 60250 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.710 mm) | HB | UL 94 | |
| Oxygen Index | 22 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 25 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 250 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65.0 - 93.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Feed Temperature: 230 to 240°CZone 4 Temperature: 240 to 260°CManifold Temperature: 250 to 260°C |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C R 218 V30 BLACK 1 N | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| Spartech Polycom SC2-1090 | Spartech Polycom | PS (HIPS) | Spartech |
| VALOX™ SHF4910 resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |
| FRblend® PBT-1301 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PBT | FRblend® |
| Polyclear® Preserve PET 2201 | Indorama Ventures Polymers México | PET | Polyclear® |