ACRYLITE® Resist ZK6SR

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Cyro LLC
Trademark:	ACRYLITE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	g1wb3Q_ACRYLITE-Resist-ZK6SR.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

ACRYLITE® Resist ZK6SR polymer is an amorphous, impact-modified thermoplastic molding and extrusion compound based on polymethyl methacrylate (PMMA).

Typical properties of ACRYLITE® Resist acrylic polymers are:

high weather resistance

high light transmission

improved resistance to stress cracking

good melt flow rate

easy to color

The special properties of ACRYLITE® Resist ZK6SR polymer are:

high impact/break resistance and strength

high melt strength for extrusion

low melt flow rate

medium heat resistance

AMECA listed as ZK6 (x)

Application:
Used for extruded sheet, co-extruded sheet and extruded profiles.

General Information
Additive	Impact Modifier
Features	Amorphous Good Colorability Good Melt Strength Good Weather Resistance High Clarity High Impact Resistance High Strength Impact Modified Low Flow Medium Heat Resistance
Uses	Appliance Components Capstock Household Goods Housings Lenses Lighting Applications Writing Instruments
Agency Ratings	EC 1907/2006 (REACH)
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Coextrusion Extrusion Injection Molding Profile Extrusion Sheet Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.16	g/cm³	ASTM D792
Apparent Density	0.71	g/cm³	ASTM D1895
Melt Mass-Flow Rate (MFR) (230°C/3.8 kg)	1.3	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.40 to 0.70	%	ASTM D955
Water Absorption (Equilibrium)	< 0.30	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	40		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1590	MPa	ASTM D638
Tensile Strength	41.4	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	5.0	%
Break	60	%
Flexural Modulus	1380	MPa	ASTM D790
Flexural Strength	55.2	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
0°C, 6.35 mm	43	J/m
23°C, 3.18 mm	59	J/m
23°C, 6.35 mm	59	J/m

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm)	82.8	°C	ASTM D648
Vicat Softening Temperature	91.1	°C	ASTM D1525
CLTE - Flow (0 to 100°C)	9.0E-5	cm/cm/°C	ASTM D696

Optical	Nominal Value	Unit	Test Method
Transmittance (3200 µm)	> 90.0	%	ASTM D1003
Haze (3200 µm)	< 2.0	%	ASTM D1003
Yellowness Index (3.20 mm)	0.20	YI	ASTM D1925

Resin Grade	Manufacturer	Category	Trademark
Moldex® QS254D/QCM240	Mitsubishi Chemical Corporation	Polyolefin, Unspecified	Moldex®
ULTEM™ 4001 resin	SABIC Innovative Plastics	PEI	ULTEM™
AKROMID® B3 1 natural (2499)	AKRO-PLASTIC GmbH	Nylon 6	AKROMID®
LNP™ LUBRICOMP™ RL0039XP compound	SABIC Innovative Plastics Europe	Nylon 66	LNP™ LUBRICOMP™
OXPEKK® IG100	Oxford Performance Materials, Inc.	PEKK	OXPEKK®