DOW™ LDPE 690 HEALTH+™
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g1u6TW_DOW-LDPE-690-HEALTH-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW™ LDPE 690 HEALTH+™ is a Low Density Polyethylene barefoot resin designed for extrusion blow molding, injection blow molding, and blow-fill seal applications with good flexibility, moderate rigidity and good chemical resistance. It is also suitable for medical packaging films. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Resistance (51 µm) | 2.90 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD : 51 µm | 159 | J/cm³ | ASTM D882 |
| TD : 51 µm | 185 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 181 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 207 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 12.3 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 12.1 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 24.8 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 23.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 420 | % | ASTM D882 |
| TD : Fracture, 51 µm | 670 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 150 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 51 µm | 500 | g | ASTM D1922 |
| TD : 51 µm | 280 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.3 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 112 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 66 | ASTM D2457 | |
| Haze (50.8 µm) | 7.6 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 232 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5mm)；30/1 比率 L/D 螺杆类型：单跨双混合 模具间隙：40 密尔 (1.6 mm) 熔体温度：450°F (199°C) 输出：模具周长的 7 磅/小时/英寸 模具直径：6 英寸 放大比：2.5 比 1 螺杆速度：60 rpm 冷冻线高度：25 英寸 (635 mm) |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SNOLEN® IM 26/59 | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| DuraSurf™ 4001 DuraJet | Crown Plastics | UHMWPE | DuraSurf™ |
| HK HIPS SR600 | Hong Kong Petrochemical Co. Ltd. | PS (HIPS) | HK HIPS |
| THERMOLAST® V TV7VAN (Series: LTP/PA) | KRAIBURG TPE | TPE | THERMOLAST® V |
| PENTAMID B S GV25 H FR natural | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |