Desmopan® DP 9662DU
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g1nlNa_Desmopan-DP-9662DU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extrusion- and injection molding grade; with special UV stabilizers; transparent up to 6 mm wall thickness; very good hydrolysis and microbial resistance; Application; Ski boot shells; Hoses, non-reinforced |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.18 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, 23°C | 97 | ||
| Shore D, 23°C | 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | DIN 53504 | ||
| Break, 23°C | 52.7 | MPa | |
| 10% Strain, 23°C | 12.3 | MPa | |
| 50% Strain, 23°C | 20.7 | MPa | |
| 100% Strain, 23°C | 26.0 | MPa | |
| 300% Strain, 23°C | 40.1 | MPa | |
| Tensile Strain 2(Break, 23°C) | 350 | % | DIN 53504 |
| Flexural Modulus 3(23°C) | 185 | MPa | ISO 178 |
| Abrasion Resistance (23°C) | 20.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 2.53 | GPa | |
| 20°C | 0.643 | GPa | |
| 60°C | 0.187 | GPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience (23°C) | 31 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4(23°C) | 98 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 59 | % | |
| 70°C, 24 hr | 87 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 110 | °C | |
| Processing (Melt) Temp | 220 to 235 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 110 | °C | |
| Melt Temperature | 205 to 235 | °C |
| Note Message | |
|---|---|
| 1 . | 200 mm/min |
| 2 . | 200 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sunny® PBT EB215 | Guangdong Shunde Shunyan New Material Co., Ltd. | PBT | Sunny® |
| Sumiflex® K K768DB6 | Mitsubishi Chemical Corporation | PVC Elastomer | Sumiflex® K |
| Veroplas PA2009L | PlastxWorld Inc. | Nylon 6 | Veroplas |
| Geon™ Vinyl Flexible 90042 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| EMVIN 733 | Intergulf Empol | PVC, Flexible | EMVIN |