ASTALAC™ ABS TX52
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g1Qb4b_ASTALAC-ABS-TX52.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALAC™ ABS TX52 is a transparent grade of ABS. It has good processability and good physical properties such as high impact strength and rigidity. It is equally at home being moulded in appliance, home wares, electronics, toys, bulk food systems and stationary applications. It has better chemical resistance than GPPS and better impact strength than SAN. ASTALAC™ ABS TX52 complies with the requirements of the (USA) FDA21 CFR181.32 (b) (3) "Acrylonitrile copolymers and resins" limitations for acrylonitrile monomer extraction |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 16 | g/10 min | |
| 230°C/3.8 kg | 7.0 | g/10 min | |
| Molding Shrinkage - Flow (3.00 mm) | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 43.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 30 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2000 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 65.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 120 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 10.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 70.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 97.0 | °C | ASTM D1525 5 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (3.00 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3000 µm) | 89.0 | % | ASTM D1003 |
| Haze (3000 µm) | 3.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 190 to 205 | °C | |
| Middle Temperature | 205 to 220 | °C | |
| Front Temperature | 220 to 235 | °C | |
| Processing (Melt) Temp | 220 to 230 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8240-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ADDILENE J 310 | ADDIPLAST | PP Copolymer | ADDILENE |
| Braskem PE SGF4950 | Braskem | HDPE | Braskem PE |
| Edgetek™ PF-05GF/000 FR MR | PolyOne Corporation | PSU | Edgetek™ |
| Kingfa MAC-601 UV | Kingfa | PC+ABS | Kingfa |