MAJORIS DFR912
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g1Q1Go_MAJORIS-DFR912.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DFR 912 is a halogen free flame retardant compound UL 94 VO , intended for injection moulding. The product is available in natural but other colours can be provided on request DFR 912 is especially designed for technical parts. In addition to having good flame retardant properties this product has an extremely low level of toxicity in case of fire. END USE DFR 912 is mainly intended for the injection moulding of electrical components. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.5 - 2.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| -15°C | 5100 | MPa | ISO 527-2 |
| 0°C | 3700 | MPa | ISO 527-2 |
| 23°C | 2800 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield, -15°C | 43.0 | MPa | ISO 527-2 |
| Yield, 0°C | 36.0 | MPa | ISO 527-2 |
| Yield, 23°C | 26.0 | MPa | ISO 527-2 |
| Fracture, -15°C | 40.0 | MPa | ISO 527-2 |
| Fracture, 0°C | 32.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, -15°C | 3.6 | % | ISO 527-2 |
| Yield, 0°C | 3.4 | % | ISO 527-2 |
| Yield, 23°C | 2.7 | % | ISO 527-2 |
| Fracture, -15°C | 5.0 | % | ISO 527-2 |
| Fracture, 0°C | 9.0 | % | ISO 527-2 |
| Fracture, 23°C | 8.0 | % | ISO 527-2 |
| Flexural Modulus 1 | 2400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180 | ||
| -15°C | 2.0 | kJ/m² | ISO 180 |
| 0°C | 2.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 99.0 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 220 | °C | |
| Mold Temperature | 50.0 - 60.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® B 218L V30 BLACK 44 N | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® B |
| Smoothblend® POM-3500 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | Acetal (POM) Homopolymer | Smoothblend® |
| TUFNYL® RGF 30 FRO GREY | SRF Ltd. | Nylon 66 | TUFNYL® |
| Nanjing Hongrui PA66 A303 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Lucent ABS ABS-45T | Lucent Polymers, Inc. | ABS | Lucent ABS |