Nypol® PA A3 M3 NTLA014 NR411 MSP
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | g1DVqe_Nypol-PA-A3-M3-NTLA014-NR411-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 natural reinforced with 3% of MoS2, high resistance to coat, good set of mechanical properties, high tenacity and elongation, good set of thermal properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.40 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.5 to 1.7 | -- | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.3 | -- | % | ASTM D570 |
| Ash Content | 2.0 to 3.0 | -- | % | ASTM D2584 |
| Relative Viscosity | 45.0 to 55.0 | -- |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | 104 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 85.0 | 70.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 57 | > 57 | % | ASTM D638 |
| Flexural Modulus | 2950 | 1250 | MPa | ASTM D790 |
| Flexural Strength | 10.0 | 65.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 50 | 60 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 65.0 | -- | °C | ASTM D648 |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 | 1.0E+13 | ohms·cm | ASTM D257 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.700 mm) | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index | 850 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® C101 | Chevron Phillips Chemical Company LLC | LLDPE | Marlex® |
| SHIN-A SEV-4315M70 | SHIN-A T&C | Epoxy | SHIN-A |
| BESTNYL SC30VI02BMU | Triesa Plastics | Nylon 66/6 | BESTNYL |
| Grivory® HTV-6H1 black 9205 | EMS-GRIVORY | Nylon 6I/6T | Grivory® |
| Pearlbond™ 580 | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Pearlbond™ |