ASTALOY™ PC/ABS TWG-28328 is a highly pigmented alloy of ABS and Polycarbonate and is designed for injection moulding applications requiring reduced light bleed and a balance of impact toughness, heat resistance, product rigidity, mouldability. Typical applications include light box display units. Note: The letters "U" as a suffix indicates UV stabilisation has been added [ ie: ASTALOY™ PC/ABS TWGU-28328 ]. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/3.8 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 100 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2400 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 450 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 40.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 100 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 106 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 110 | °C | |
| Vicat Softening Temperature | 133 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 100 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 235 to 255 | °C | |
| Middle Temperature | 245 to 265 | °C | |
| Front Temperature | 255 to 275 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trademark PP PPC2040M | Trademark Plastics Corporation | PP Impact Copolymer | Trademark PP |
| Borealis PP BB412E | Borealis AG | PP Copolymer | Borealis PP |
| COPEC® CC7OCZ (Series: VS/AD1) | KRAIBURG TPE | TPE | COPEC® |
| ICORENE® N2807 | ICO Polymers EMEA, A Division of A. Schulman | HDPE | ICORENE® |
| MAJORIS DWB304X | AD majoris | PP, Unspecified | MAJORIS |